A Comparative study of the firing shrinkage properties of the process temperature control rings

Abstract

A process temperature control ring was developed from talc, magnesium carbonate, barium carbonate, iron oxide, kaolin, and quartz.  The rings were formed by the dry pressing method into a diameter of 2.5 cm and with the density of 1.8 g/cm³.  The firing shrinkages of rings at 960°C, 1100°C, 1140°C, and 1200°C varied in the range of 2.21-9.98 % with the standard deviation varied in the range of 0.00-0.06. In this study, the properties of the rings were statistical analyzed. It was found that an increasing temperature resulted in an increasing firing shrinkage but  no effect on the standard deviation values.  The study also presented the comparative properties of the rings with the commercial ones in terms of the average firing shrinkage, the standard deviation and the change of the shrinkage with temperature.

บทคัดย่อ

อุปกรณ์ตรวจสอบอุณหภูมิแบบวงกลมได้พัฒนาจากสูตรที่ประกอบด้วย ทัลคัม แมกนีเซียมคาร์บอเนต แบเรียมคาร์บอเนต เหล็กออกไซด์ ดินขาว และควอตซ์ เป็นองค์ประกอบ ขึ้นรูปอุปกรณ์ฯด้วยวิธีอัดแห้งให้ได้ขนาดเส้นผ่านศูนย์กลาง 2.5 ซม. ความหนาแน่น 1.8 กรัม/ลบ.ซม. ตัวอย่างมีสมบัติการหดตัวเมื่อเผาที่อุณหภูมิ 960 ํC, 1100 ํC,1140 ํC และ 1200 ํC อยู่ในช่วงร้อยละ 2.21-9.98 และมีค่าส่วนเบี่ยงเบนมาตรฐาน 0.00-0.06 งานวิจัยนี้ได้ใช้สถิติในการประมวลผลสมบัติของอุปกรณ์ฯที่พัฒนาเมื่อเผา พบว่าการเพิ่มอุณหภูมิมีผลให้การหดตัวเมื่อเผาเพิ่มขึ้น แต่ไม่มีผลต่อค่าส่วนเบี่ยงเบนมาตรฐานของการหดตัวเมื่อเผา งานวิจัยนี้ยังได้แสดงข้อมูลเปรียบเทียบสมบัติของอุปกรณ์ฯที่พัฒนากับอุปกรณ์ฯที่จำหน่ายในท้องตลาด ในค่าเฉลี่ยของการหดตัวเมื่อเผา ค่าส่วนเบี่ยงเบนมาตรฐานของการหดตัว เมื่อเผา และการเปลี่ยนแปลงของค่าการหดตัวเมื่อเผากับระดับอุณหภูมิ